All Products > For Low Alloy
Steel
|
|
Brand Name
|
Type of covering
|
Equivalent Specification
|
Welding Position
|
Type of
Current |
Chemical Composition of Wire(%)
|
Mechanical Properties
of Deposited Metal |
Applications
|
| C |
Mn |
Si |
S |
P |
Cr |
Ni |
Mo |
V |
Y.P.(MPa) |
T.S. (MPa)
|
EL.(%) L=5d
|
Typical
I.V.(J) |
| CHE506NiLH |
Extra Low hydrogen
potassium |
AWS E7016-G
GB E5016-G |
F,V,
OH,H |
AC or DC+
|
<=0.12
0.07 |
>=1.00
1.10 |
<=0.60
0.40 |
<=0.035
0.020 |
<=0.035
0.020 |
- |
<=0.60
0.45 |
- |
- |
>=390
440 |
>=490
550 |
>=22
30 |
-20oC
-45oC
150
100 |
Welding of important
mild steel and made of low alloy steel structures, such as
offshore drilling platforms, bridges, high pressure vessels,
ships, etc. |
| CHE507NiLH |
Extra Low hydrogen
sodium |
AWS E7015-G
GB D5015-G |
F,V,
OH,H |
DC+ |
-
0.07 |
>=1.00
1.10 |
<=0.60
0.40 |
-
0.020 |
-
0.020 |
- |
<=0.60
0.45 |
- |
- |
>=390
440 |
>=490
550 |
>=22
30 |
-20oC
-45oC
150
100 |
Welding of important
mild steel and made of low alloy steel structures, such as
bridges, offshore drilling platforms and high pressure vessels
etc. |
| CHE508N |
Iron powder Low
hydrogen potassium |
AWS E7018-G
GB E5018-G |
F,V,
OH,H |
AC or DC+
|
-
0.08 |
>=1.00
1.20 |
<=0.80
0.35 |
-
0.010 |
-
0.015 |
- |
>=0.50
0.80 |
- |
- |
>=390
440 |
>=490
550 |
>=22
30 |
-20oC -45oC -60oC
130 100
60 |
Welding of low
alloy steel structures with corresponding grade in strength.
|
| CHE557 |
Low hydrogen sodium
|
AWS E8015-G
GB D5515-G |
F,HF |
DC+ |
<=0.12
0.08 |
>=1.00
1.20 |
<=0.80
0.45 |
<=0.035
0.020 |
<=0.035
0.020 |
- |
- |
- |
- |
>=440
460 |
>=540
580 |
>=17
25 |
-40oC
60 |
Welding of medium
carbon steel structures and low alloy steel structures
|
| CHE557MoV |
Low hydrogen
sodium |
AWS E8015-G
GB E5515-G |
F,V,
OH,H |
DC+ |
<=0.12
0.07 |
>=0.80
0.90 |
<=0.25
0.20 |
<=0.035
0.020 |
<=0.035
0.020 |
- |
|
>=0.15
0.25 |
>=0.03
0.04 |
>=440
460 |
>=540
580 |
>=17
25 |
-40oC
80 |
Welding of low
alloy steel structures with corresponding grade strength.
|
| CHE606 |
Low hydrogen
potassium |
AWS E9016-G
GB E6016-G |
F,V,
OH,H |
AC or DC+
|
<=0.12
0.07 |
1.25-1.75
1.30 |
<=0.60
0.45 |
<=0.035
0.020 |
<=0.035
0.020 |
- |
|
0.25-0.45
0.30 |
- |
>=490
540 |
>=590
660 |
>=15
22 |
-50oC
50 |
Welding of medium
carbon steel and low alloy high tensile steel structures with
corresponding grade of strength. AC can be used in cases where
no DC welding set is |
| CHE607 |
Low hydrogen sodium
|
AWS E7016-G
GB E5016-G |
F,V,
OH,H |
DC+ |
<=0.12
0.08 |
1.25-1.75
1.50 |
<=0.60
0.45 |
<=0.035
0.020 |
<=0.035
0.020 |
- |
|
0.25-0.45
0.30 |
- |
>=490
550 |
>=590
660 |
>=15
22 |
-50oC
80 |
Welding of medium
carbon steel and low alloy steel with corresponding grade
of strength. |
| CHE607Ni |
Low hydrogen sodium
|
AWS E7015-G
GB E5015-G |
F,V,
OH,H |
DC+ |
<=0.12
0.08 |
>=1.00
1.50 |
<=0.80
0.40 |
<=0.035
0.015 |
<=0.035
0.020 |
- |
>=0.50
0.75 |
>=0.20
0.35 |
- |
>=490
550 |
>=590
660 |
>=15
22 |
-50oC
50 |
Welding of low
alloy steel structures with corresponding grade of strength.
|
| CHE62CF |
Low hydrogen sodium
|
AWS E9015-G
JIS D6015 |
F,V,
OH,H |
DC+ |
<=0.08
0.06 |
>=1.00
1.20 |
<=0.25
0.10 |
<=0.035
0.020 |
<=0.035
0.020 |
- |
<=0.60
0.45 |
>=0.15
0.25 |
<=0.08
0.05 |
>=490
550 |
>=590
660 |
>=15
24 |
-20oC
75 |
Welding of medium-sheets
made of 62CF with corresponding grade of strength.
|
| CHE62CFLH |
Extra Low hydrogen
sodium |
AWS E9015-G
JIS D6015 |
F,V,
OH,H |
DC+ |
<=0.08
0.06 |
>=1.00
1.20 |
<=0.50
0.30 |
<=0.030
0.010 |
<=0.030
0.020 |
- |
<=1.00
0.80 |
>=0.15
0.25 |
- |
>=490
550 |
>=590
660 |
>=15
24 |
-20oC
-50oC
100
50 |
Welding of medium-sheets
made of 62CF with corresponding grade of strength.
|
| CHE707 |
Low hydrogen sodium
|
AWS E10015-G
GB E7015-G |
F,V,
OH,H |
DC+ |
<=0.12
0.07 |
1.65-2.00
1.68 |
<=0.60
0.55 |
<=0.035
0.020 |
<=0.035
0.020 |
- |
- |
0.25-0.45
0.42 |
- |
>=590
620 |
>=690
750 |
>=15
20 |
-50oC
60 |
Welding of medium
carbon steel structures and low alloy steel structures
|
| CHE707Ni |
Low hydrogen sodium
|
AWS E10015-G
GB E7015-G |
F,V,
OH,H |
DC+ |
<=0.15
0.07 |
>=1.00
1.50 |
<=0.80
0.45 |
<=0.030
0.010 |
<=0.030
0.020 |
>=0.30
0.40 |
>=1.50
1.60 |
>=0.20
0.45 |
- |
>=590
630 |
>=690
750 |
>=15
24 |
-40oC
-50oC
80
60 |
Welding of low
alloy steel structures with corresponding grade of strength.
|
| CHE707MnMo |
Low hydrogen sodium
|
AWS E10015-G
GB E7015-G |
F,V,
OH,H |
DC+ |
<=0.10
0.07 |
>=1.00
1.40 |
0.30-0.80
0.60 |
<=0.035
0.020 |
<=0.035
0.020 |
- |
- |
>=0.30
0.45 |
- |
>=590
620 |
>=690
750 |
>=15
20 |
20oC
120 |
Welding of low
alloy steel structures with corresponding 690MPa tensile strength.
|
| CHE757 |
Low hydrogen sodium
|
AWS E11015-G
GB D7515-G |
F,V,
OH,H |
DC+ |
<=0.15
0.08 |
>=1.00
1.40 |
<=0.60
0.45 |
<=0.030
0.010 |
<=0.030
0.020 |
- |
- |
<=1.00
0.50 |
- |
>=640
680 |
>=740
820 |
>=13
20 |
20oC
80 |
Welding of low
alloy steel with corresponding 740MPa tensile strength.
|
| CHE758 |
Low hydrogen potassium
|
AWS E11018-G
GB E7518-G |
F,V,
OH,H |
AC or DC+
|
<=0.10
0.06 |
>=1.00
1.30 |
<=0.60
0.30 |
<=0.030
0.015 |
<=0.030
0.020 |
>=0.80
0.40 |
<=0.60
0.45 |
>=0.20
0.30 |
<=0.10
0.01 |
>=640
680 |
>=740
820 |
>=13
20 |
-30oC
-50oC
80
50 |
Welding of low
alloy steel with corresponding 740MPa tensile strength.
|
| CHE80C |
Low hydrogen sodium
|
AWS E12015-G
|
F,V,
OH,H |
DC+ |
<=0.12
0.07 |
>=1.00
1.70 |
<=0.60
0.40 |
<=0.030
0.010 |
<=0.030
0.020 |
>=0.50
0.20 |
<=2.55
2.20 |
>=0.30
0.08 |
|
>=690
720 |
>=780
850 |
>=13
20 |
-15oC
-40oC
80
50 |
Welding of low
alloy steel with corresponding 780MPa tensile strength.
|
| CHE857 |
Low hydrogen sodium
|
AWS E12015-G
GB E8515-G |
F,V,
OH,H |
DC+ |
<=0.15
0.10 |
>=1.00
1.60 |
<=0.40
0.60 |
<=0.035
0.010 |
<=0.035
0.020 |
- |
- |
>=0.60
0.80 |
- |
>=740
780 |
>=830
900 |
>=12
18 |
20oC
80 |
Welding of low
alloy steel structures with corresponding 830MPa tensile strength.
|
| CHE857Cr |
Low hydrogen sodium
|
AWS E9016-G
GB E8515-G |
F,V,
OH,H |
DC+ |
<=0.15
0.10 |
>=1.00
1.60 |
<=0.80
0.50 |
<=0.035
0.010 |
<=0.035
0.020 |
>=0.70
0.80 |
- |
>=0.50
0.80 |
>=0.50
0.10 |
>=740
780 |
>=830
900 |
>=12
18 |
20oC
80 |
Welding of low
alloy steel pressure vessels and other structures with corresponding
830MPa tensile strength. |
| CHE857CrNi |
Low hydrogen sodium
|
AWS E12015-G
GB E8515-G |
F,V,
OH,H |
DC+ |
<=0.10
0.06 |
>=1.30
1.60 |
<=0.80
0.35 |
<=0.035
0.012 |
<=0.035
0.015 |
>=0.30
0.50 |
><=1.75
2.00 |
>=0.30
0.45 |
<=0.05
0.01 |
>=740
760 |
>=830
860 |
>=12
18 |
-50oC
50 |
Welding of low
alloy steel structures with corresponding 830MPa tensile strength,
such as WEL-TEN80,WEL-TEN80C etc |
| CHE858 |
Iron powder Low
hydrogen potassium |
AWS E12018-G
GB E8515-G |
F,V,
OH,H |
AC or DC+
|
<=0.10
0.07 |
>=1.30
1.50 |
<=0.80
0.30 |
<=0.035
0.015 |
<=0.035
0.020 |
>=0.30
0.50 |
>=1.75
1.80 |
>=0.30
0.40 |
<=0.05
0.01 |
>=740
780 |
>=830
900 |
>=12
18 |
-30oC
-50oC
70
50 |
Welding of low
alloy steel structures with corresponding 830MPa tensile strength,
such as WEL-TEN80,WEL-TEN80C etc |
|
|